Industry Norms
Test Results
Thickness
0.8mm mm (± 10%)
0.8mm (± 5%)
Resistance to surface wear
= 350 (revolutions)
> >350 (revolutions)
Resistance to immersion in boiling water Mass increase (%)
12.0% (Max)
7.0% (Max)
Resistance to immersion in boiling water Thickness increase (%)
14.0% (Max)
8.0% (Max)
Resistance to dry heat 180� C
Should pass test
Passed
Dimensional stability at deviated temperature Longitudinal (%)
0.625% (Max)
0.40% (Max)
Dimensional stability at deviated temperature Transverse (%)
1.10% (Max)
0.80% (Max)
Dimensional stability at 20� C Longitudinal (%)
0.425% (Max)
0.32% (Max)
Dimensional stability at 20� C Transverse (%)
0.625% (Max)
0.52% (Max)
Resistance to impact by small diameter ball
20N (Min)
2.5 N (Min)
Resistance to cracking
Should pass test
Passed
Resistance to scratching
2N (Min)
2.5N (Min)
Resistance to staining
Should pass test
Passed
Resistance to colour change In Xenon light
Should pass test
Passed
Resistance to colour change In Enclosed Carbon ARC light
Should pass test
Passed
Resistance to cigarette burns
Should pass test
Passed
Resistance to steam
Should pass test
Passed
Appearance
No ABC Defects
No ABC Defects
Specific gravity gm/c.m3
N/A
1.33 (Min)
This is the 0.8mm laminates range from the house of CenturyPly
A fabulous collection from the house of CenturyLaminates offers: Greater Power to Resist Abrasion
Higher Colourfastness Best bonding with substrates due to A Very Uniform & Superior Sanding
Product confirms to International Standards set by ISO 4586-1 & IS 2046
All sheets are marked with "ISI" license No. CM/L 5237965