CENTURYPLY PRELAMINATED MDF
AND PARTICLE BOARD
CENTURYPLY Prelam, a high
class Prelaminated board is
introduced in the market in the
year 2005 by Century Plyboards
(I) Ltd, a dynamic and fast
growing Industrial house of India.Centuryply Prelam is made
from superfine and closed
surface superior quality
imported boards which are
pressed and laminated on both
surfaces with specially
formulated MF resin impregnated
imported base paper under
influence of heat and pressure
in a fully automated and advance
single day-light short cycle
press.
|
 |
QUALITY:
Centuryply is
a brand known in the domestic
and international market for its
consistent quality product with
difference. Quality control and
quality assurance department of
Centuryply consist of a team of
highly qualified and experienced
professionals with all
ultramodern equipments and
instruments facilities ensure
consistent quality in raw
materials, production processes
and finished goods.
Centuryply prelam particleboard
conforms to IS-12823 BIS license
CM/L No. 5248061
Centuryply prelam MDF conforms
to IS- 14587:1998 applied for
BIS license.
AVAILABILITY:
1.
Category: Prelam MDF &
Prelam P.B
2. Finishes: Suede &
Matt.
3. Sizes:
MDF:
Available in 8x4 ft size only.
P.B:
Available in 9x6, 8x6, 8x4, 8x3,
6x4, 6x3, 7x6, 7x5 ft.
4.
Thickness:
MDF:
8mm, 12mm, 18mm, 25 mm.
P.B: 9
mm, 12mm, 18mm, 25mm.
WHY
CENTURYPLY PRELAM?
1. A wide
range of shades in pastel and
wood grains.
2. Widest range of sizes
including unique size of 7x5 ft.
3. Matching post-forming
laminates are available.
4. Matching edge binder are also
available
5. Environmental friendly
product. Substrate boards are
made from pine wood meeting E1
grade of European Standard. |
| SL |
Properties |
UIS 12823 : 1990 Requirements |
Centuryply Prelaminated Particle Board |
|
1 |
Length (mm) |
2440 +06 / -0 |
1441 |
|
2 |
Width (mm) |
1220 +03/ -0 |
1222 |
|
3 |
Thickness (mm) |
18 ± 5% |
18.08 |
|
4 |
Straightness (mm) / Meter |
2 mm Per 1000 mm |
1mm |
|
5 |
Square ness (mm) / Meter |
2 mm Per 1000 mm |
1mm |
|
6 |
Appearance |
No A,B, C Defects |
Defect Free |
|
7 |
Density Kg / Cu M |
500 - 900 |
710 |
|
8 |
Density Variation % ,( Max.) |
± 10 |
2.5 |
|
9 |
Water absorption % (Max ) |
|
|
a) 2 hours |
15 |
9.2 |
|
|
b) 24 hours |
30 |
26.2 |
|
10 |
Thickness swelling %, 2 hours , (Max ) |
8 |
6.2 |
|
11 |
Modulus of rupture N/Sq mm( Min )Average |
11 |
11.8 |
|
|
Min. Individual |
10 |
10.8 |
|
12 |
Tensile strength perpendicular to |
|
|
to surface ( Min ) , N/ Sq mm |
0.3 |
0.43 |
|
13 |
Screw withdrawal strength ( Min ) N |
|
|
a) Face |
1250 |
1475 |
|
|
b) Edge |
750 |
950 |
|
14 |
Modulus of Elasticity N/Sq mm (min)Average |
2500 |
2580 |
|
|
Min. Individual |
2200 |
2380 |
|
15 |
Abrasion Resistance ( min ) in no |
|
|
of revolutions |
450 |
485 |
|
16 |
Moisture Content % |
5 - 15 |
7.5 |
|
17 |
Resistance to steam |
Shall not show any sign of blister,
delamination or change in surface finish |
Passed |
|
18 |
Crack Resistance |
Shall not show any sign ofcracks or
delamination |
Passed |
|
19 |
Resistance to Cigarette Burn |
Shall not leave any mark or stain |
Passed |
|
20 |
Resistance to Stain |
Shall not leave any mark or stain |
Passed |
|